High thermoelectric performance of flexible nanocomposite films based on Bi2Te3 nanoplates and carbon nanotubes selected using ultracentrifugation

Scientific Reports volume 13, Article number: 3010 (2023) Cite this article

1054 Accesses

3 Citations

1 Altmetric

Metrics details

Thermoelectric generators with flexibility and high performance near 300 K have the potential to be employed in self-supporting power supplies for Internet of Things (IoT) devices. Bismuth telluride (Bi2Te3) exhibits high thermoelectric performance, and single-walled carbon nanotubes (SWCNTs) show excellent flexibility. Therefore, composites of Bi2Te3 and SWCNTs should exhibit an optimal structure and high performance. In this study, flexible nanocomposite films based on Bi2Te3 nanoplates and SWCNTs were prepared by drop casting on a flexible sheet, followed by thermal annealing. Bi2Te3 nanoplates were synthesized using the solvothermal method, and SWCNTs were synthesized using the super-growth method. To improve the thermoelectric properties of the SWCNTs, ultracentrifugation with a surfactant was performed to selectively obtain suitable SWCNTs. This process selects thin and long SWCNTs but does not consider the crystallinity, chirality distribution, and diameters. A film consisting of Bi2Te3 nanoplates and the thin and long SWCNTs exhibited high electrical conductivity, which was six times higher than that of a film with SWCNTs obtained without ultracentrifugation; this is because the SWCNTs uniformly connected the surrounding nanoplates. The power factor was 6.3 μW/(cm K2), revealing that this is one of the best-performing flexible nanocomposite films. The findings of this study can support the application of flexible nanocomposite films in thermoelectric generators to provide self-supporting power supplies for IoT devices.

Thin-film thermoelectric generators (TEGs) are gaining increasing interest as power supplies for sensors and Internet of Things (IoT) devices1,2,3,4. TEGs produce electrical power from various heat sources, such as the human body, industrial waste heat, and natural heat5,6,7. The power supplies for sensors and IoT devices must possess flexibility and a small size but need not generate high electric power8. The requirements of sensors and IoT devices align with the characteristics of thin-film TEGs. The efficiency of a TEG directly depends on the performance of the thermoelectric material, which is expressed as the dimensionless figure of merit (ZT), defined as ZT = σS2T/κ, and the power factor (PF), defined as PF = σS2, where σ, S, and κ are the electrical conductivity, Seebeck coefficient, and thermal conductivity, respectively.

Among thermoelectric materials, bismuth telluride (Bi2Te3) and carbon nanotubes (CNTs) are the primary candidates for the aforementioned applications. Bi2Te3 was developed in the 1950s and exhibits the highest thermoelectric performance near 300 K9,10. Bi2Te3 has a rhombohedral tetradymite-type crystal structure, with the space group \(D_{3d}^{5} (R\mathop 3\limits^{ - } m)\), and its unit cell is described as hexagonal. Owing to this structure, Bi2Te3 crystals are grown as hexagonal nanoplates in the solution process11,12,13. Bi2Te3 nanoplates are approximately 1 μm in diameter and tens of nanometers in thickness. This structure contributes to improving the thermoelectric performance owing to the low-dimensional effect and quantum size effect14,15,16. In previous studies, hexagonal Bi2Te3 nanoplates were synthesized by solvothermal synthesis under various conditions17,18,19, and Bi2Te3 nanoplate films were prepared using drop-casting20,21,22,23. Furthermore, CNTs are classified into multi-walled CNTs (MWCNTs), fabricated in 1991, and single-walled CNTs (SWCNTs), fabricated in 199324,25. MWCNTs exhibit metallic characteristics and SWCNTs exhibit metallic or semiconducting characteristics depending on their structure, which is characterized by the chiral index (n,m)26. SWCNTs with semiconducting characteristics have been used as thermoelectric materials27,28,29,30,31. The performance of SWCNTs is inferior to that of Bi2Te3, but SWCNTs have excellent characteristics, including flexibility, heat resistance, and nontoxicity. Therefore, many researchers have attempted to improve the thermoelectric performance of SWCNTs32,33,34,35,36.

A favorable approach for improving thermoelectric performance is to fabricate nanocomposites based on Bi2Te3 nanoplates and semiconducting SWCNTs37,38,39. Jin et al. reported a flexible thermoelectric material composed of highly ordered Bi2Te3 nanocrystals anchored on an SWCNT network31. Hosokawa and Takashiri and Yabuki et al. developed nanocomposite films based on Bi2Te3 nanoplates and SWCNTs by drop-casting followed by thermal annealing40,41. A key factor for increasing the thermoelectric performance of nanocomposites is the quality of SWCNTs. As-synthesized SWCNTs (pristine SWCNTs) exhibit many types of structures with different lengths and chiralities42,43. When the optimal SWCNTs with suitable structures are selected, the thermoelectric performance of nanocomposite films based on Bi2Te3 nanoplates and SWCNTs can be further improved.

In this study, ultracentrifugation is performed for the selection of SWCNTs. Ultracentrifugation is known to select SWCNTs based on their length and chirality in a scalable manner44,45,46,47. Bi2Te3 nanoplates are prepared via solvothermal synthesis. The dispersion solution is formed with the selected SWCNTs and Bi2Te3 nanoplates, and the nanocomposite films are formed on a flexible sheet using the solution by drop-casting, which is a simple and cost-effective wet process. For comparison, pristine SWCNTs are used to form nanocomposite films. The structure and thermoelectric properties of the nanocomposite films are analyzed, and the effectiveness of the selection of SWCNTs is evaluated.

A schematic diagram of the fabrication process of flexible nanocomposite films based on Bi2Te3 nanoplates and SWCNTs is shown in Fig. 1. The Bi2Te3 nanoplates were synthesized using a solvothermal method. The detailed experimental setup was described in detail in previous reports21,48. Briefly, the system comprised a stainless-steel autoclave with a built-in Teflon container, a hot plate with a magnetic stirrer, and heat blocks. The precursor solution and stir bar were placed in an autoclave with an internal volume of 50 cm3. The solvents used were analytical-grade Bi2O3 (purity 99.9%, Fujifilm Wako Co.), TeO2 (purity 99.9%, Kojundo Chemical Laboratory), ethylene glycol (purity 99.5%, Fujifilm Wako Co.), polyvinylpyrrolidone (PVP) (purity 99.9%, Fujifilm Wako Co., K30, Ms ~ 40,000), and sodium hydroxide (NaOH) (purity > 97.0%, Fujifilm Wako Chemical Co.) without further purification. Bi2Te3 nanoplates were fabricated according to the following procedure: 0.4 g of PVP was dissolved in ethylene glycol (18 mL), followed by the addition of Bi2O3 (20 mM), TeO2 (70 mM), and 2 mL of NaOH solution (5.0 M). The resulting precursor solution was then sealed in an autoclave. The autoclave was then heated and maintained at 200 °C for 4 h, with stirring at 500 rpm. After the synthesis, the products were allowed to cool naturally below 70 °C. The products were then collected by centrifugation and washed several times with distilled water and absolute ethanol. Finally, the products were dried under a vacuum at 60 °C for 24 h.

Fabrication process of nanocomposite flexible films based on Bi2Te3 nanoplates and selected SWCNTs using ultracentrifugation.

Super-growth carbon nanotubes (SGCNTs) (ZEONANO SG101, purity > 99%, ZEON) were used as SWCNTs. The dispersion solution was prepared by adding 0.5 wt.% of SGCNT powder in 6 mL of ethanol, followed by homogeneously dispersing it using an ultrasonic homogenizer (Emerson SFX25) at 20 W for 45 min. As a surfactant, 2 mL of a sodium dodecylbenzene sulfonate (SDBS) standard solution (Fujifilm Wako Co.) was added to the dispersion solution, followed by stirring at 500 rpm for 30 min using a stirrer (AZ-1 Corporation DP-1L). The dispersion solution (3 mL) was placed in a centrifuge tube, and ultracentrifugation was performed at a rotation speed of 46,000 rpm (average force of 88,000 g) for 1 h. The weight fraction of SWCNTs in the supernatant layer was approximately 10% of the initial amount of SWCNTs used in the solution.

The process conditions for preparing the nanocomposite films were determined based on our previous report40. After ultracentrifugation, 1 mL from the top of the solution and 1 mL from the bottom were extracted, and 10 mg of Bi2Te3 nanoplates were added to each solution. The solution was then drop-casted onto a polyimide substrate using a metal wall. The nanocomposite films were 22 mm long and 12 mm wide, with a thickness of approximately 2 μm. After drying the nanocomposite films in air, they were thermally annealed at 250 °C to evaporate residual solvents in the thin films and to completely connect the Bi2Te3 nanoplates and SWCNTs. A heating furnace was filled with a mixture of Ar (95%) and H2 (5%) at atmospheric pressure. The temperature was maintained at 250 °C for 1 h. Following thermal annealing, the samples were allowed to cool naturally below 70 °C in the furnace. The flexibility of the nanocomposite films was confirmed using the bending test. To evaluate the effect of ultracentrifugation, nanocomposite films composed of Bi2Te3 nanoplates and SWCNTs were prepared with no ultracentrifugation, that is, with pristine SWCNTs, under the same preparation conditions.

The precise structure of the Bi2Te3 nanoplates was analyzed using high-resolution transmission electron microscopy (TEM) (JEOL JEM-ARM200F) and selected-area electron diffraction (SAED) at an accelerating voltage of 200 kV. The phase purity and crystal structure of the nanoplates were characterized by X-ray diffraction (XRD) (D8 ADVANCE) using Cu-Kα radiation (λ = 0.154 nm, with 2θ ranging from 10° to 80°). The atomic composition of the nanoplates was determined using an electron probe microanalyzer (EPMA, Shimazu, EPMA-1600) and calibrated using the ZAF4 program supplied with the EPMA-1610 device.

The crystallinity and characteristics of the SWCNTs were characterized using Raman spectroscopy with a 532 nm laser source wavelength (XploRA HORIBA). The morphologies of the nanocomposite films of Bi2Te3 nanoplates and SWCNTs were investigated using field-emission scanning electron microscopy (Hitachi S-4800). The precise morphology and structure of the SWCNTs were analyzed by high-resolution TEM (JEOL JEM-2100F) at an accelerating voltage of 200 kV. The in-plane electrical conductivities (σ) of the samples were measured at 300 K using a four-point probe method (Napson RT-70V). The in-plane Seebeck coefficients (S) of the samples were measured at 300 K49,50,51. One end of the film was connected to a heat sink, and the other end was connected to a heater. Two 0.1-mm-diameter K-type thermocouples, placed 13 mm apart, were pressed near the center of the thin films. The temperature difference between the thermocouples was varied from 1 to 4 K, and the thermoelectric voltage was recorded at intervals of 1 K. The Seebeck coefficient was estimated according to the V-K slope using a linear approximation. The in-plane power factor (σS2) was obtained from the experimentally measured electrical conductivity and the Seebeck coefficient.

A TEM image of a typical Bi2Te3 nanoplate is shown in Fig. 2a. The Bi2Te3 nanoplates exhibited a regular hexagonal shape with an approximate lateral size of 1–2 μm. The nanoplates were sufficiently thin (less than 50 nm) that the overlap of the nanoplates could be observed. The SAED pattern shown in the inset of Fig. 2a was indexed to the [00l] zone axis of rhombohedral Bi2Te3, indicating that the nanoplate was single crystalline. The high-resolution TEM (HRTEM) image in the inset of Fig. 2a shows that the lattice fringes were also structurally uniform, with a spacing of 0.21 nm, which is in good agreement with the d value of the (110) planes of rhombohedral Bi2Te3. The phase purity and crystal structure of the Bi2Te3 nanoplates were examined using XRD analysis, as shown in Fig. 2b. The peaks observed in the XRD patterns of the nanoplates were indexed to the standard diffraction pattern of Bi2Te3 (JCPDS 15-0863). The main peaks were observed in the c-axis-oriented (00l), (015), and (1010) planes. The atomic ratio of nanoplates (Te/(Bi + Te)) determined using EPMA analysis was 60.6 at.%, which was very close to the stoichiometric proportion of 60.0 at.%. In addition, oxygen was detected in the EPMA analysis, indicating either adsorption of oxygen molecules on the nanoplate surface or formation of natural oxide layers.

(a) TEM image of Bi2Te3 nanoplates prepared by solvothermal synthesis. The insets show the HRTEM image and SAED pattern. (b) X-ray diffraction patterns of the Bi2Te3 nanoplates.

The Raman spectra of the SWCNTs in the top and bottom solutions are shown in Fig. 3. For comparison, the Raman spectra of the SDBS are shown in the figure. The Raman spectra of the SWCNTs in the top solution included the peaks of the SWCNTs and SDBS, whereas those of the SWCNTs in the bottom solution only exhibited the peaks of the SWCNTs, even though the cleaning process of the SWCNTs after ultracentrifugation was the same for the top and bottom solutions. This indicates that the molecules of SDBS were more firmly attached to the SWCNT surface in the top solution. The intensity ratio of the G and D bands, IG/ID, which shows the crystallinity of SWCNTs, was 1.1 and 1.3 for the SWCNTs in the top and bottom solutions, respectively. Therefore, the crystallinity of the SWCNTs did not vary significantly between the top and bottom solutions. In the inset of Fig. 3, the SWCNTs in the top and bottom solutions exhibited several radial breathing mode (RBM) peaks in the range of 100–400 cm−1, indicating that SWCNTs with different chirality distributions and diameters existed. Consequently, the crystallinity, chirality distribution, and diameters of the SWCNTs were not selected by ultracentrifugation.

Raman spectra of SWCNTs in the top and bottom solutions. The inset shows a detailed analysis of the RBM modes ranging from 100 to 400 cm-1.

Figure 4 shows SEM images of the surface morphologies of the nanocomposite films with Bi2Te3 nanoplates and SWCNTs obtained from different positions in the aforementioned solution. For comparison, the SEM image of the nanocomposite film with pristine SWCNTs is shown in Fig. 4a. Regular hexagonal Bi2Te3 nanoplates, with an average diameter of approximately 1 μm, were relatively well-aligned. There were variations in the diameter of the SWCNT bundles, and the maximum diameter observed was approximately 100 nm. The SWCNT bundles were observed by HRTEM, as shown in the inset of Fig. 4a. Owing to the uneven distribution of the SWCNT bundles, the positions at which nanoplates could be connected were limited. Upon using the SWCNTs in the top solution (Fig. 4b), the Bi2Te3 nanoplates were relatively well-aligned to the in-plane direction. The diameters of the SWCNT bundles were significantly smaller than those of the pristine SWCNT bundles, as shown in Fig. 4a. This indicates that the SWCNT bundles were unraveled by ultracentrifugation, which is revealed by the HRTEM image in the inset of Fig. 4b. Many thin and long SWCNTs were uniformly attached to the Bi2Te3 nanoplates. As the length of the SWCNTs was longer than that of the nanoplates, the SWCNT connected the surrounding nanoplates. The location of yellow arrows in the figure shows the most typical SWCNTs. When the SWCNTs in the bottom solution were used (Fig. 4c), thin SWCNTs were observed on the surface of the nanoplates, and the SWCNT connected the surrounding nanoplates. The diameter of the SWCNTs in the bottom solution was comparable to that of the SWCNTs in the top solution, which was observed by the HRTEM image shown in the inset of Fig. 4c.

SEM image of nanocomposite films based on Bi2Te3 nanoplates and different SWCNTs. The insets show the HRTEM images of each SWCNT. (a) Pristine SWCNTs, (b) SWCNTs in the top solution, and (c) SWCNTs in the bottom solution.

The thermoelectric properties of the nanocomposite films are presented in Table 1. The electrical conductivity of the film with SWCNTs from the top solution was 370 S/cm, which was approximately six times higher than that of the film with SWCNTs from the bottom solution. The clear mechanism could not be identified. However, a possible explanation is that the SWCNTs in the top solution were firmly coated with the residual surfactant, as shown in Fig. 3, and that the residual surfactant contributed to a strong connection between the SWCNTs and nanoplates52. Consequently, sodium ions in the SDBS surfactants were considered to increase the electrical conductivity. The detailed analysis of the mechanism should be performed using a molecular dynamics simulation in the future. The electrical conductivity of the film with pristine SWCNTs was also low, possibly because the current path was restricted owing to the non-uniform distribution of the SWCNT bundles41. The Seebeck coefficient of the film with SWCNTs from the top solution was exhibited at n-type characteristic and a value of − 131 μV/K, which was approximately 10% higher than those of the films with SWCNTs from the bottom solution and pristine SWCNTs. The phenomena occurred because of the decreasing contact resistance between the SWCNTs and nanoplates. The power factor of the film with SWCNTs from the top solution was 6.3 μW/(cm K2), which was approximately eight times higher than that of the films with SWCNTs from the bottom solution and pristine SWCNTs, mainly because of the significant increase in electrical conductivity. As a result, by performing ultracentrifugation with the SDBS surfactant to select the SWCNTs, the power factor can be greatly improved. The thermoelectric properties of flexible nanocomposite films were compared to those of flexible nanocomposite films reported in the literature. The power factor of the nanocomposite films of Bi2Te3 nanoplates/SWCNTs (top) was higher than that of the nanocomposite film with SWCNTs using similar wet processes and with reduced graphene oxide nanosheets (rGO)53,54,55. However, the top value in this study was lower than the value (18.4 μW/(cm⋅K2) of flexible nanocomposite film using a sputtering (dry process), possibly because highly oriented nanoplates were obtained31. Therefore, the selection of SWCNTs using ultracentrifugation with a surfactant improved the thermoelectric performance via a simple and cost-effective method. To further enhance the performance, an effective way is to improve the orientation of the nanoplates by optimizing the process.

To improve the thermoelectric performance of nanocomposite films based on Bi2Te3 nanoplates and SWCNTs, ultracentrifugation was used to select suitable SWCNTs. After ultracentrifugation, the dispersion solution was divided into two parts, the top and the bottom, and each part was dried. The SWCNTs from each part were mixed with Bi2Te3 nanoplates in ethanol and flexible nanocomposite films were prepared on a polyimide sheet by drop casting. The nanocomposite film fabricated with SWCNTs from the top solution exhibited a higher electrical conductivity than that of the nanocomposite films with SWCNTs from the bottom solution and SWCNTs without ultracentrifugation. This phenomenon occurred possibly because the residual surfactant contributed to a strong connection between the SWCNTs and nanoplates. In future work, several other approaches will be further investigated to deduce the mechanism. The power factor was 6.3 μW/(cm K2), revealing that this was one of the best-performing flexible nanocomposite films. Therefore, this study demonstrated an improvement in the thermoelectric performance of nanocomposite films by the selection of SWCNTs using ultracentrifugation with a surfactant. The findings of this study can support the application of nanocomposite films in TEGs for providing self-supporting power supplies for IoT devices. Further research should focus on increasing the electrical conductivity while maintaining a high Seebeck coefficient.

The datasets used and/or analyzed during the current study available from the corresponding author on reasonable request.

Rojas, J. P. et al. Review—Micro and nano-engineering enabled new generation of thermoelectric generator devices and applications. ECS J. Solid State Sci. Technol. 6, N3036–N3044 (2017).

Article CAS Google Scholar

Yamamuro, H., Hatsuta, N., Wachi, M., Takei, Y. & Takashiri, M. Combination of electrodeposition and transfer processes for flexible thin-film thermoelectric generators. Coatings 8, 22 (2018).

Article Google Scholar

Kobayashi, A., Konagaya, R., Tanaka, S. & Takashiri, M. Optimized structure of tubular thermoelectric generators using n-type Bi2Te3 and p-type Sb2Te3 thin films on flexible substrate for energy harvesting. Sens. Actuators A 313, 112199 (2020).

Article CAS Google Scholar

Kuang, N., Zuo, Z., Wang, W., Liu, R. & Zhao, Z. Optimized thermoelectric properties and geometry parameters of annular thin-film thermoelectric generators using n-type Bi2Te2.7Se0.3 and p-type Bi0.5Sb1.5Te3 thin films for energy harvesting. Sens. Actuators A 332, 113030 (2021).

Article CAS Google Scholar

Madan, D., Wang, Z., Wright, P. K. & Evans, J. W. Printed flexible thermoelectric generators for use on low levels of waste heat. Appl. Energy 156, 587–592 (2015).

Article CAS Google Scholar

Hyland, M., Hunter, H., Liu, J., Veety, E. & Vashaee, D. Wearable thermoelectric generators for human body heat harvesting. Appl. Energy 182, 518–524 (2016).

Article Google Scholar

Siddique, A. R. M., Mahmud, S. & Van Heyst, B. A review of the state of the science on wearable thermoelectric power generators (TEGs) and their existing challenges. Renew. Sustain. Energy Rev. 73, 730–744 (2017).

Article Google Scholar

Leonov, V., Torfs, T., Fiorini, P. & Hoof, C. V. Thermoelectric converters of human warmth for self-powered wireless sensor nodes. IEEE Sens. J. 7, 650–657 (2007).

Article ADS Google Scholar

Harman, T. C., Paris, B., Miller, S. E. & Goering, H. L. Preparation and some physical properties of Bi2Te3, Sb2Te3, and As2Te3. J. Phys. Chem. Solids 2, 181–190 (1957).

Article ADS CAS Google Scholar

Satterthwaite, C. B. & Ure, R. W. Jr. Electrical and thermal properties of Bi2Te3. Phys. Rev. 108, 1164–1170 (1957).

Article ADS CAS Google Scholar

Fan, X. A. et al. Bi2Te3 hexagonal nanoplates and thermoelectric properties of n-type Bi2Te3 nanocomposites. J. Phys. D Appl. Phys. 40, 5975–5979 (2007).

Article ADS CAS Google Scholar

Liang, Y. et al. Influence of NaOH on the formation and morphology of Bi2Te3 nanostructures in a solvothermal process: From hexagonal nanoplates to nanorings. Mater. Chem. Phys. 129, 90–98 (2011).

Article CAS Google Scholar

Hollar, C. et al. High-performance flexible bismuth telluride thin film from solution processed colloidal nanoplates. Adv. Mater. Technol. 5, 2000600 (2020).

Article CAS PubMed PubMed Central Google Scholar

Hicks, L. & Dresselhaus, M. S. Effect of quantum-well structures on the thermoelectric figure of merit. Phys. Rev. B 47, 12727–12731 (1993).

Article ADS CAS Google Scholar

Venkatasubramaian, R., Siivola, E., Colpitts, T. & O’Quinn, B. Thin-film thermoelectric devices with high room-temperature figures of merit. Nature 413, 597–602 (2001).

Article ADS Google Scholar

Harman, T. C., Taylor, P. J., Walsh, M. P. & LaForge, B. E. Quantum dot superlattice thermoelectric materials and devices. Science 297, 2229–2232 (2002).

Article ADS CAS PubMed Google Scholar

Takashiri, M., Kai, S., Wada, K., Takasugi, S. & Tomita, K. Role of stirring assist during solvothermal synthesis for preparing single-crystal bismuth telluride hexagonal nanoplates. Mater. Chem. Phys. 173, 213–218 (2016).

Article CAS Google Scholar

Hosokawa, Y., Tomita, K. & Takashiri, M. Growth of single-crystalline Bi2Te3 hexagonal nanoplates with and without single nanopores during temperature-controlled solvothermal synthesis. Sci. Rep. 9, 10790 (2019).

Article ADS PubMed PubMed Central Google Scholar

Yamazaki, H., Eguchi, R. & Takashiri, M. Investigation of phase transition from critical nucleus to Bi2Te3 nanoplate based on screw dislocation-driven spiral growth by solvothermal synthesis. Cryst. Res. Technol. 56, 2100153 (2021).

Article CAS Google Scholar

Wada, K., Tomita, K. & Takashiri, M. Fabrication of bismuth telluride nanoplates via solvothermal synthesis using different alkalis and nanoplate thin films by printing method. J. Cryst. Growth 468, 194–198 (2017).

Article ADS CAS Google Scholar

Hosokawa, Y., Wada, K., Tanaka, M., Tomita, K. & Takashiri, M. Thermal annealing effect on structural and thermoelectric properties of hexagonal Bi2Te3 nanoplate thin films by drop-casting technique. Jpn. J. Appl. Phys. 57, 02CC02 (2018).

Article Google Scholar

Mori, R. et al. Measurement of thermal boundary resistance and thermal conductivity of single-crystalline Bi2Te3 nanoplate films by differential 3ω method. Appl. Phys. Express 13, 035501 (2020).

Article ADS CAS Google Scholar

Kimura, Y. et al. Solvothermal synthesis of n-type Bi2(SexTe1−x)3 nanoplates for high-performance thermoelectric thin films on flexible substrates. Sci. Rep. 10, 6315 (2020).

Article ADS CAS PubMed PubMed Central Google Scholar

Iijima, S. & Ichihashi, T. Single-shell carbon nanotubes of 1-nm diameter. Nature 363, 603–605 (1993).

Article ADS CAS Google Scholar

Iijima, S. Helical microtubules of graphitic carbon. Nature 354, 56–58 (1991).

Article ADS CAS Google Scholar

Karousis, N., Tagmatarchis, N. & Tasis, D. Current progress on the chemical modification of carbon nanotubes. Chem. Rev. 110, 5366–5397 (2010).

Article CAS PubMed Google Scholar

Avery, A. D. et al. Tailored semiconducting carbon nanotube networks with enhanced thermoelectric properties. Nat. Energy 1, 16033 (2016).

Article ADS CAS Google Scholar

Blackburn, J. L. et al. Intrinsic and extrinsically limited thermoelectric transport within semiconducting single-walled carbon nanotube networks. Adv. Electron. Mater. 5, 1800910 (2019).

Article CAS Google Scholar

Nakai, Y. et al. Giant Seebeck coefficient in semiconducting single-wall carbon nanotube film. Appl. Phys. Express 7, 025103 (2014).

Article ADS CAS Google Scholar

Ichinose, Y. et al. Solving the thermoelectric trade-off problem with metallic carbon nanotubes. Nano Lett. 19, 7370–7376 (2019).

Article ADS CAS PubMed Google Scholar

Jin, Q. et al. Flexible layer-structured Bi2Te3 thermoelectric on a carbon nanotube scaffold. Nat. Mater. 18, 62–68 (2019).

Article ADS CAS PubMed Google Scholar

Macleod, B. A. et al. Large n- and p-type thermoelectric power factors from doped semiconducting single-walled carbon nanotube thin films. Energy Environ. Sci. 10, 2168–2179 (2017).

Article CAS Google Scholar

Hata, S. et al. Enhancement of p-type thermoelectric power factor by low-temperature calcination in carbon nanotube thermoelectric films containing cyclodextrin polymer and Pd. Appl. Phys. Lett. 118, 243904 (2021).

Article ADS CAS Google Scholar

Seki, Y., Nagata, K. & Takashiri, M. Facile preparation of air-stable n-type thermoelectric single-wall carbon nanotube films with anionic surfactants. Sci. Rep. 10, 8104 (2020).

Article ADS CAS PubMed PubMed Central Google Scholar

Yonezawa, S., Chiba, T., Seki, Y. & Takashiri, M. Origin of n type properties in single wall carbon nanotube films with anionic surfactants investigated by experimental and theoretical analyses. Sci. Rep. 11, 5758 (2021).

Article ADS CAS PubMed PubMed Central Google Scholar

Chiba, T., Amma, Y. & Takashiri, M. Heat source free water floating carbon nanotube thermoelectric generators. Sci. Rep. 11, 14707 (2021).

Article ADS CAS PubMed PubMed Central Google Scholar

Kim, K.-T. et al. The influence of CNTs on the thermoelectric properties of a CNT/Bi2Te3 composite. Carbon 52, 541–549 (2013).

Article CAS Google Scholar

Liu, Y., Du, Y., Meng, Q., Xu, J. & Shen, S. Z. Effects of preparation methods on the thermoelectric performance of SWCNT/Bi2Te3 bulk composites. Materials 13, 2636 (2020).

Article ADS CAS PubMed PubMed Central Google Scholar

Ahmad, K. & Wan, C. Enhanced thermoelectric performance of Bi2Te3 through uniform dispersion of single wall carbon nanotubes. Nanotechnology 28, 415402 (2017).

Article PubMed Google Scholar

Hosokawa, Y. & Takashiri, M. Impact of the amount of single-wall carbon nanotubes (SWCNTs) in single-crystalline Bi2Te3 nanoplates/SWCNTs nanocomposite films by drop-casting method. Jpn. J. Appl. Phys. 58, SDDG04 (2019).

Article CAS Google Scholar

Yabuki, H., Yonezawa, S., Eguchi, R. & Takashiri, M. Flexible thermoelectric films formed using integrated nanocomposites with single-wall carbon nanotubes and Bi2Te3 nanoplates via solvothermal synthesis. Sci. Rep. 10, 17031 (2020).

Article ADS CAS PubMed PubMed Central Google Scholar

Liu, B., Wu, F., Gui, H., Zheng, M. & Zhou, C. Chirality-controlled synthesis and applications of single-wall carbon nanotubes. ACS Nano 11, 31–53 (2017).

Article CAS PubMed Google Scholar

Chiba, T., Seki, Y. & Takashiri, M. Correlation between the air stability of n-type thermoelectric properties and defects in single-walled carbon nanotubes with anionic surfactants. AIP Adv. 11, 015332 (2021).

Article ADS CAS Google Scholar

Arnold, M. S., Green, A. A., Hulvat, J. F., Stupp, S. I. & Hersam, M. C. Sorting carbon nanotubes by electronic structure using density differentiation. Nat. Nanotechnol. 1, 60–65 (2006).

Article ADS CAS PubMed Google Scholar

Fagan, J. A., Becker, M. L., Chun, J. & Hobbie, E. K. Length fractionation of carbon nanotubes using centrifugation. Adv. Mater. 20, 1609–1613 (2008).

Article CAS Google Scholar

Green, A. A. & Hersam, M. C. Ultracentrifugation of single-walled nanotubes. Mater. Today 10, 59–60 (2007).

Article CAS Google Scholar

O’Connell, M. J. et al. Band gap fluorescence from individual single-walled carbon nanotubes. Science 297, 593–596 (2002).

Article ADS PubMed Google Scholar

Wada, K., Tomita, K. & Takashiri, M. Thermoelectric properties of bismuth telluride nanoplate thin films determined using combined infrared spectroscopy and first-principles calculation. Jpn. J. Appl. Phys. 57, 06HC02 (2018).

Article Google Scholar

Matsuoka, K., Okuhata, M. & Takashiri, M. Dual-bath electrodeposition of n-type Bi-Te/Bi-Se multilayer thin films. J. Alloys Compd. 649, 721–725 (2015).

Article CAS Google Scholar

Inamoto, T. & Takashiri, M. Experimental and first-principles study of the electronic transport properties of strained Bi2Te3 thin films on a flexible substrate. J. Appl. Phys. 120, 125105 (2016).

Article ADS Google Scholar

Kudo, S., Tanaka, S., Miyazaki, K., Nishi, Y. & Takashiri, M. Anisotropic analysis of nanocrystalline bismuth telluride thin films treated by homogeneous electron beam irradiation. Mater. Trans. 58, 513–519 (2017).

Article CAS Google Scholar

Tkalya, E. E., Ghislandi, M., de With, G. & Koning, C. E. The use of surfactants for dispersing carbon nanotubes and graphene to make conductive nanocomposites. Curr. Opin. Colloid Interface Sci. 17, 225–232 (2012).

Article CAS Google Scholar

Chen, Z., Lv, H., Zhang, Q., Wang, H. & Chen, G. Construction of a cement–rebar nanoarchitecture for a solution-processed and flexible film of a Bi2Te3/CNT hybrid toward low thermal conductivity and high thermoelectric performance. Carbon Energy 4, 115–128 (2021).

Article ADS Google Scholar

Chen, X. et al. Flexible thermoelectric films based on Bi2Te3 nanosheets and carbon nanotube network with high n-type performance. ACS Appl. Mater. Interfaces 13, 5451–5459 (2021).

Article CAS PubMed Google Scholar

Ding, D., Sun, F., Xia, F. & Tang, Z. A high-performance and flexible thermoelectric generator based on the solution-processed composites of reduced graphene oxide nanosheets and bismuth telluride nanoplates. Nanoscale Adv. 2, 3244–3251 (2020).

Article ADS CAS PubMed PubMed Central Google Scholar

Download references

This study was partially supported by JSPS KAKENHI (Grant Number: 20H02576) and the business development of joint research in industry and academia at Hiratsuka city and Kanto Yakin Kogyo Corporation. The authors wish to thank H. Uchida at Zeon Corporation, E. Shindo at Tokyo City University, N. Kojima, K. Tomita, and M. Morikawa at Tokai University for providing experimental support.

Department of Materials Science, Tokai University, Hiratsuka, Kanagawa, 259-1292, Japan

Tomoyuki Chiba, Hayato Yabuki & Masayuki Takashiri

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

T.C.: investigation, visualization, writing—original draft, writing—review and editing. H.Y.: conceptualization, investigation, visualization. M.T.: resources, writing—original draft, writing—review and editing, supervision, funding acquisition.

Correspondence to Masayuki Takashiri.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Chiba, T., Yabuki, H. & Takashiri, M. High thermoelectric performance of flexible nanocomposite films based on Bi2Te3 nanoplates and carbon nanotubes selected using ultracentrifugation. Sci Rep 13, 3010 (2023). https://doi.org/10.1038/s41598-023-30175-0

Download citation

Received: 05 June 2022

Accepted: 17 February 2023

Published: 21 February 2023

DOI: https://doi.org/10.1038/s41598-023-30175-0

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Scientific Reports (2023)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.